LNP™ COLORCOMP™ HF1140RC compound

Category: PC , Polycarbonate
Manufacturer: SABIC Innovative Plastics
Trademark: LNP™ COLORCOMP™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: CKOV6v_LNPCOLORCOMPHF1140RCcompound.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
COLORCOMP* HF1140RC is a compound based on Polycarbonate Resin. Added features include: High Flow, Heat Stabilized, Mold Release, FDA Food Contact Compliant. Not to be used for medical applications which require biocompatibility.
General Information
Additive
  • heat stabilizer
Features
  • High liquidity
  • Thermal Stability
  • Compliance of Food Exposure
  • Good demoulding performance
Agency Ratings
  • FDA Food Exposure, Not Rated
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity ASTM D792
    -- 1.20g/cm³ASTM D792
    -- 1.19g/cm³ASTM D792
Specific Volume 0.830cm³/gASTM D792
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)25g/10 minASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)23.0cm³/10minISO 1133
Molding Shrinkage - Flow (3.20 mm)0.50 - 0.70%Internal method
Water Absorption ASTM D570
    24 hr 0.15%ASTM D570
    Equilibrium, 23°C 0.35%ASTM D570
    Equilibrium, 100°C 0.58%ASTM D570
HardnessNominal ValueUnitTest Method
Rockwell Hardness ASTM D785
    Class m 70ASTM D785
    Class r 118ASTM D785
MechanicalNominal ValueUnitTest Method
Tensile Modulus
    -- 12370MPaASTM D638
    -- 2350MPaISO 527-2/1
Tensile Strength
    Yield 262.0MPaASTM D638
    Yield 63.0MPaISO 527-2/50
    Fracture 365.0MPaASTM D638
    Fracture 50.0MPaISO 527-2/50
Tensile Elongation
    Yield 46.0%ASTM D638
    Yield 6.0%ISO 527-2/50
    Fracture 5120%ASTM D638
    Fracture 70%ISO 527-2/50
Flexural Modulus
    50.0mm span 62300MPaASTM D790
    -- 72300MPaISO 178
Flexural Stress
    -- 90.0MPaISO 178
    Yield, 50.0mm span 893.0MPaASTM D790
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)10.0mgASTM D1044
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength 9ISO 179/1eA
    -30°C 10kJ/m²ISO 179/1eA
    23°C 12kJ/m²ISO 179/1eA
Notched Izod Impact
    Natural, Tints 640J/mASTM D256
    23°C 640J/mASTM D256
    -30°C 1010kJ/m²ISO 180/1A
    23°C 1112kJ/m²ISO 180/1A
Unnotched Izod Impact (23°C)3200J/mASTM D4812
Instrumented Dart Impact (23°C, Energy at Peak Load)54.0JASTM D3763
Dart Drop Impact (23°C)169JASTM D3029
Tensile Impact Strength 12378kJ/m²ASTM D1822
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load
    0.45 MPa, unannealed, 6.40mm 137°CASTM D648
    0.45 MPa, unannealed, 100 mm span 13133°CISO 75-2/Be
    1.8 MPa, unannealed, 3.20mm 126°CASTM D648
    1.8 MPa, unannealed, 6.40mm 126°CASTM D648
    1.8 MPa, unannealed, 100 mm span 14121°CISO 75-2/Ae
Vicat Softening Temperature
    -- 145°CISO 306/A50
    -- 139°CISO 306/B50
    -- 140°CISO 306/B120
Ball Pressure Test (125°C)PassIEC 60695-10-2
CLTE - Flow
    -40 to 95°C 6.8E-5cm/cm/°CASTM E831
    23 to 80°C 7.0E-5cm/cm/°CISO 11359-2
Specific Heat 1250J/kg/°CASTM C351
Thermal Conductivity
    -- 0.19W/m/KASTM C177
    -- 0.20W/m/KISO 8302
RTI Elec 130°CUL 746
RTI Imp 130°CUL 746
RTI 130°CUL 746
ElectricalNominal ValueUnitTest Method
Surface Resistivity > 1.0E+15ohmsIEC 60093
Volume Resistivity
    -- > 1.0E+17ohms·cmASTM D257
    -- > 1.0E+15ohms·cmIEC 60093
Dielectric Strength
    3.20 mm, in Air 15kV/mmASTM D149
    0.800mm, in oil 35kV/mmIEC 60243-1
    1.60mm, in oil 27kV/mmIEC 60243-1
    3.20mm, in oil 17kV/mmIEC 60243-1
Dielectric Constant
    50 Hz 3.17ASTM D150
    60 Hz 3.17ASTM D150
    1 MHz 2.96ASTM D150
    50 Hz 2.70IEC 60250
    60 Hz 2.70IEC 60250
    1 MHz 2.70IEC 60250
Dissipation Factor
    50 Hz 9.0E-4ASTM D150
    60 Hz 9.0E-4ASTM D150
    1 MHz 0.010ASTM D150, IEC 60250
    50 Hz 1.0E-3IEC 60250
    60 Hz 1.0E-3IEC 60250
Comparative Tracking Index (CTI) PLC 2UL 746
High Amp Arc Ignition (HAI) PLC 1UL 746
High Voltage Arc Tracking Rate (HVTR) PLC 2UL 746
Hot-wire Ignition (HWI) PLC 2UL 746
FlammabilityNominal ValueUnitTest Method
Flame Rating (1.1 mm)V-2UL 94
Oxygen Index 25%ISO 4589-2
OpticalNominal ValueUnitTest Method
Refractive Index 1.586ASTM D542
Transmittance (2540 µm)88.0%ASTM D1003
Haze (2540 µm)1.0%ASTM D1003
InjectionNominal ValueUnit
Drying Temperature 121°C
Drying Time 3.0 - 4.0hr
Drying Time, Maximum 48hr
Suggested Max Moisture 0.020%
Suggested Shot Size 40 - 60%
Rear Temperature 249 - 271°C
Middle Temperature 260 - 282°C
Front Temperature 271 - 293°C
Nozzle Temperature 266 - 288°C
Processing (Melt) Temp 271 - 293°C
Mold Temperature 71 - 93°C
Back Pressure 0.345 - 0.689MPa
Screw Speed 40 - 70rpm
Vent Depth 0.025 - 0.076mm
Note Message
1 .50 mm/min
2 .Type 1, 50mm/min
3 .Type 1, 50mm/min
4 .Type 1, 50mm/min
5 .Type 1, 50mm/min
6 .1.3 mm/min
7 .2.0 mm/min
8 .1.3 mm/min
9 .80*10*4 sp=62mm
10 .80*10*4
11 .80*10*4
12 .Type S
13 .120*10*4 mm
14 .120*10*4 mm
Resin Grade Manufacturer Category Trademark
Rilsan® MB 3610 Noir Arkema Nylon 11 Rilsan®
NEXUS Reprocessed PPC 10/2 RBK Nexus Resin Group, LLC. PP Copolymer NEXUS Reprocessed
Chemraz XCD Greene, Tweed & Co. Perfluoroelastomer Chemraz
Glastic® 1608 Bulk Molding Compounds, Inc. Polyester, TS Glastic®
Sylvin 9077-85 Grey 9334 Sylvin Technologies Incorporated PVC, Unspecified Sylvin

TEL: +86-21-58958519 Email:sales@su-jiao.com

No. 215, Lianhe North Road, Fengxian District, Shanghai, China​， COPYRIGHT SUSHENG COMPANY RIGHTS RESERVED