UTTAP SF 600
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | UTTAP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CIycN7_UTTAP-SF-600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyether Sulfone Resin - Medium Viscosity, un-reinforced standard grade for easy injection molding. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 2600 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 23°C) | 88.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus 4(23°C, 50.0 mm Span) | 2800 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 23°C, 50.0 mm Span) | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 195 | °C | ASTM D648 |
| Glass Transition Temperature | 225 | °C | ASTM E1356 |
| Additional Information |
|---|
| DTUL @ 264psi, ASTM D648, Unannealed, 3.2 mm: > 195 mmThe value listed as Glass Transition Temp, ASTM E1356 was tested in accordance with ASTM D3482. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 X 119106 H | RTP Company | Nylon 66 | RTP |
| ULTEM™ PW2300 resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |
| Next Nylon 66 Prime Series PXR-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| BESTNYL SI30VI02ANU | Triesa Plastics | Nylon 6 | BESTNYL |
| Latilub 62-15ST | LATI S.p.A. | Nylon 6 | Latilub |