Xuchuan A-8070/B-8016 is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) product. It is available in Asia Pacific. Typical application: Consumer Goods. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.400 to 0.600 | g/cm³ | |
| Density | |||
| A-8070 : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-8016 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-8070 : 40°C | 1.00 to 1.40 | Pa·s | |
| B-8016 : 40°C | 0.600 to 0.800 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Ross Flex (23°C) 1 | No Crack |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 8.0 to 10.0 | sec | |
| End of Rise Time | 1.0 to 1.2 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 240 to 260 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 6.0 to 8.0 | hr | |
| Part B | 8.0 to 12.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 38 to 42 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 to 75 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 3.20 to 4.00 | MPa | |
| Tensile Elongation (Break) | 340 to 450 | % | |
| Tear Strength | 16.0 to 25.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 80 to 82 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 45.0 to 55.0 | °C |
| Note Message | |
|---|---|
| 1 . | 40000 cycles |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP510L | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Nipol® 1577K | Zeon Corporation | Latex | Nipol® |
| ENGAGE™ HM 7387 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| Later 4 G/30-V0HF1 | LATI S.p.A. | PBT | Later |
| PERLEX® R2510 | A. Schulman Europe | PC | PERLEX® |