LNP™ COLORCOMP™ D1000P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CINqkY_LNP-COLORCOMP-D1000P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP D1000P is an unfilled Polycarbonate. Added feature of this grade is: Exceptional Processing. Also known as: LNP* COLORCOMP* Compound D-1000 EP Product reorder name: D1000P |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.75 | % | ISO 294-4 |
| Flow : 24 hr | 0.65 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2210 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 62.1 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2 |
| Break | 56.5 | MPa | ASTM D638 |
| Break | 59.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.3 | % | ASTM D638 |
| Yield | 5.6 | % | ISO 527-2 |
| Break | 79 | % | ASTM D638 |
| Break | 87 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Stress | 81.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 540 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 124 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8828-74 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 4LOY® 10E17200 | 4Plas | PC+ABS | 4LOY® |
| Americas Styrenics EC6600 | Americas Styrenics LLC | PS (HIPS) | Americas Styrenics |
| Fainplast PVC PM 84 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Shida 100 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |