Optema™ TC 114 Blown
| Category: | EMA , Ethylene Methyl Acrylate Copolymer Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Optema™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CHrSGB_Optema-TC-114-Blown.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OPTEMA TC 114 is an ethylene-methyl acrylate copolymer, specially developed for extruding properties for blown film applications. It can be used to produce soft elastic films with good operability without additional additives. OPTEMA TC 114 can be used to produce films with a thickness of less than 1.0 mils. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Methyl Acrylate Content | 18.0 | wt% | ExxonMobil Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 49.4 | MPa | ASTM D882 |
| 1% secant, TD | 51.4 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 19.7 | MPa | ASTM D882 |
| TD : Fracture | 19.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 380 | % | ASTM D882 |
| TD : Fracture | 670 | % | ASTM D882 |
| Dart Drop Impact | 370 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 45 | g | ASTM D1922 |
| TD | 310 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 57.0 | °C | ASTM D1525 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REPROCESSED POMC M270-100R | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REPROCESSED |
| Akulon® K223-HM6 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Cawiton® MT920 | Wittenburg B.V. | SEBS | Cawiton® |
| Fortron® 0320 | Celanese Corporation | PPS | Fortron® |
| Hifax TKC 461P 3004 | LyondellBasell Industries | PP Copolymer | Hifax |