Aristech Quarite®
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CHmffl_Aristech-Quarite-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Aristech Quarite® is an Acrylic material. It is available in North America for thermoforming. Important attributes of Aristech Quarite® are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption 2(Saturation, 3.30 mm) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness 3(M-Scale, 3.30 mm) | 90 to 100 | ASTM D785 | |
| Barcol Hardness 4(3.30 mm) | 48 to 52 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 5(3.30 mm) | 3420 | MPa | ASTM D638 |
| Tensile Strength 6(Yield, 3.30 mm) | 66.9 | MPa | ASTM D638 |
| Tensile Elongation 7(Break, 3.30 mm) | 4.6 | % | ASTM D638 |
| Flexural Modulus 8(3.30 mm) | 3250 | MPa | ASTM D790 |
| Flexural Strength 9(3.30 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 10(3.30 mm) | 21 | J/m | ASTM D256A |
| Instrumented Dart Impact 11 | 3.80 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 12(1.8 MPa, Unannealed, 3.30 mm) | 87.2 | °C | ASTM D648 |
| CLTE - Flow 13(3.30 mm) | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat 14 | 1460 | J/kg/°C | ASTM C351 |
| Thermal Conductivity 15 | 0.20 | W/m/K | Internal Method |
| Thermal Stability 16(180°C, 3.18 to 3.43 mm) | No Effect | ASTM D4802 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Forming Temperature (3.18 to 3.43 mm) | 177 to 193 | °C | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 17(3.30 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 0.125 to 0.135 in |
| 2 . | 0.125 to 0.135 in |
| 3 . | 0.125 to 0.135 in |
| 4 . | 0.125 to 0.135 in |
| 5 . | 0.125 to 0.135 in |
| 6 . | 0.125 to 0.135 in |
| 7 . | 0.125 to 0.135 in |
| 8 . | 0.125 to 0.135 in |
| 9 . | 0.125 to 0.135 in |
| 10 . | 0.125 to 0.135 in |
| 11 . | 0.125 to 0.135 in, FTMS 406 M-1074 |
| 12 . | 0.125 to 0.135 in |
| 13 . | 0.125 to 0.135 in |
| 14 . | 0.125 to 0.135 in |
| 15 . | 0.125 to 0.135 in |
| 16 . | 30 min |
| 17 . | 0.125 to 0.135 in |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-HM-FR2 | Polymer Resources Ltd. | PC | PRL |
| Shandong PA66 FRPA66 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| Sumikon® EME-6300HD | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| LNP™ LUBRICOMP™ Lexan_LF0335 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| LNP™ STAT-KON™ DD000 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |