ZYLAR® 650
| Category: | MMBS , Methyl Methacrylate Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | ZYLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CHmUbq_ZYLAR-650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Zylar® 650 is an impact modified styrene acrylic copolymer that provides a balance of clarity and toughness, with outstanding strength and rigidity. Zylar 650 also has superior processing characteristics for demanding injection molded applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption | |||
| Saturation, 23°C | 0.10 | % | ASTM D570, ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 2140 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 26.2 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 48.3 | MPa | ASTM D790 |
| -- | 48.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Gardner Impact | 16.9 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 91.7 | °C | |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 1 |
| Maximum Service Temperature | 250 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 2 | 1.570 | ASTM D542 | |
| Transmittance (550 nm) | 90.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 185 to 220 | °C | |
| Front Temperature | 190 to 225 | °C | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 30.0 to 55.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | Sodium D Line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNEP® E4450 | Tyne Plastics LLC. | PET | TYNEP® |
| Network Polymers PP PPB 25 0802 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Karina BLACK PVC COMPOUD -E 901-48/ 1-F-ISM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubriOne™ PS-30GF/2S Natural | PolyOne Corporation | PBT | LubriOne™ |
| Sumiliteresin® PR-NR-1 | SBHPP | Phenolic | Sumiliteresin® |