TARFLON™ G-2515V
| Category: | PC , Polycarbonate |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CGt97K_TARFLON-G-2515V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant V-2 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 2.30 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.60 | % | |
| Flow : 2.00 mm | 0.30 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.11 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 73 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 87.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Flexural Stress | 134 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| 0°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 147 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 143 | °C | ISO 75-2/A |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC-GF15< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG3 | Shanghai Potomer International Trade Co., Ltd. | PVC, Flexible | Shanghai Potomer |
| MTM® 56 series | Cytec Industries Inc. | Epoxy | MTM® |
| Geon™ Vinyl Flexible A48248D | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Grilamid® XE 4174 black 9992 | EMS-GRIVORY | Nylon 1010 | Grilamid® |
| Elvakon® 4453 | Lucite International Holland BV | Acrylic (PMMA) | Elvakon® |