Silamid® G5
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CGXecK_Silamid-G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6, filled with graphite, improved sliding properties, optimal fluidity of mould. Injection mouldings with requirements of reducing friction coefficient, the sliding additive is released from moulding at wearing and acts as a lubricant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow | 1.2 | 1.2 | % | |
| Flow | 1.2 | 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | 0.80 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3900 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | 50.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2600 | 1200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 150 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/A |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zythane® 9085A | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| BESTPOM C09U/02 | Triesa Plastics | Acetal (POM) Copolymer | BESTPOM |
| Karina CLEAR PVC COMPOUND -E 52/205-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ EX11402 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| Plaslube® AC-80/TF/30 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |