EVALENE® LLDPE LF08262

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	JG Summit Petrochemical Corporation
Trademark:	EVALENE® LLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	CGGDwN_EVALENELLDPELF08262.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Stiff, strong and tough films are made using EVALENE ® LF08262, the most versatile EVALENE ® grade. EVALENE ® LF08262 has outstanding mechanical properties comparable with premium octene-based (C8) LLDPE, which makes it particularly suitable for very demanding heavy duty applications. EVALENE ® LF08262 can replace butene (C4) LLDPE with downgauging possibilities, and delivers maximum performance benefits as a core layer material in coextrusion.

FEATURES

Outstanding overall strength

Superior stiffness

Excellent mechanical properties

Meets FDA Philippines food-contact requirements

Halal certified

TYPICAL APPLICATIONS

Heavy duty sacks

Agricultural films

High-performance flexible and industrial packaging requiring superior puncture and tear resistance

General Information
Features	Low density Rigid, good High strength hexene comonomer Perforation resistance Good tear strength Good toughness Compliance of Food Exposure
Uses	Blown Film Packaging Films Industrial application Agricultural application Heavy packing bag
Forms	Particle
Processing Method	Film extrusion Blow film Co-extrusion molding

Physical	Nominal Value	Unit	Test Method
Density ¹	0.926	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.80	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus ²			ASTM D882
1% secant, MD : 25 µm, blown film	327	MPa	ASTM D882
1% secant, TD : 25 µm, blown film	262	MPa	ASTM D882
Tensile Strength ³			ASTM D882
MD : Yield, 25 µm, blown film	14.0	MPa	ASTM D882
TD : Yield, 25 µm, blown film	16.0	MPa	ASTM D882
MD : Broken, 25 µm, blown film	13.0	MPa	ASTM D882
TD : Broken, 25 µm, blown film	15.0	MPa	ASTM D882
Tensile Elongation ⁴			ASTM D882
MD : Yield, 25 µm, blown film	16	%	ASTM D882
TD : Yield, 25 µm, blown film	11	%	ASTM D882
MD : Broken, 25 µm, blown film	490	%	ASTM D882
TD : Broken, 25 µm, blown film	470	%	ASTM D882
Dart Drop Impact (25 µm, Blown Film)	100	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, blown film	380	g	ASTM D1922
TD : 25 µm, blown film	480	g	ASTM D1922

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.0 µm, Blown Film)	72		ASTM D2457
Haze (25.0 µm, Blown Film)	15	%	ASTM D1003

Additional Information	Nominal Value
Blow-up Ratio	2.00 - 4.00

Extrusion	Nominal Value	Unit
Melt Temperature	170 - 210	°C

Note Message
1 .	23°C
2 .	25 mm/min
3 .	500 mm/min
4 .	500 mm/min

Resin Grade	Manufacturer	Category	Trademark
Premier PH200NS	Premier Polymers, LLC.	PP Homopolymer	Premier
DOW™ LDPE 132I	The Dow Chemical Company	LDPE	DOW™ LDPE
Cellophane™ 330XSCd	Innovia Films Ltd.	Cellulose, Regenerated	Cellophane™
Fluon® PTFE RB2515	Asahi Glass Co., Ltd.	PTFE	Fluon®
Kumho ASA XC190BM	Korea Kumho Petrochemical Co., Ltd.	ASA	Kumho ASA