TOTAL Polyethylene HDPE 6410
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CEXgum_TOTAL-Polyethylene-HDPE-6410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene 6410 is a high density (MMW) polyethylene material,. This product is available in North America or Asia Pacific region. The processing method is: film extrusion or co-extrusion molding. The main features of TOTAL Polyethylene 6410 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 1.2 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 33 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus 1 | ASTM D882A | ||
| 1% secant, MD : 25 µm, blown film | 862 | MPa | ASTM D882A |
| 2% secant, MD : 25 µm, blown film | 689 | MPa | ASTM D882A |
| 1% secant, TD : 25 µm, blown film | 883 | MPa | ASTM D882A |
| 2% secant, TD : 25 µm, blown film | 703 | MPa | ASTM D882A |
| Tensile Strength 2 | ASTM D882A | ||
| MD : Yield, 25 µm, blown film | 26.2 | MPa | ASTM D882A |
| TD : Yield, 25 µm, blown film | 27.6 | MPa | ASTM D882A |
| MD : Broken, 25 µm, blown film | 51.7 | MPa | ASTM D882A |
| TD : Broken, 25 µm, blown film | 23.4 | MPa | ASTM D882A |
| Tensile Elongation 3 | ASTM D882A | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| TD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 24 | g | ASTM D1922 |
| TD : 25 µm, blown film | 390 | g | ASTM D1922 |
| Water Vapor Transmission Rate (38°C, 25 µm, Blown Film) | 6.2 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 134 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (25.4 µm, Blown Film) | 50 | ASTM D523 | |
| Haze (25.4 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| WVTR, ASTM E96, 100°F, Blown Film, 1 mil: 0.4 g/100in²/day |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4195 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SLOVALEN® PC 56 FRD 3 T 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| APEX® RE 8218A | Teknor Apex Company | PVC, Rigid | APEX® |
| Fainplast PVC PK 6010 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| HiFill® PS GL30 | Techmer Engineered Solutions | PS (GPPS) | HiFill® |