Lustran® ABS 256
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CERT0X_Lustran-ABS-256.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran ABS 256 resin is a natural, medium-flow, medium-impact, low-gloss, low-gel extrusion grade of ABS (Acrylonitrile Butadiene Styrene). It is used for blending with other Lustran ABS virgin and regrind materials to optimize cost and performance. As with any product, use of Lustran ABS 256 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Volume | 9.50E-4 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 48 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 85 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 160 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Peak Energy | 12.0 | J | ASTM D3763 |
| -40°C, Total Energy | 14.0 | J | ASTM D3763 |
| -18°C, Peak Energy | 15.0 | J | ASTM D3763 |
| -18°C, Total Energy | 16.0 | J | ASTM D3763 |
| 23°C, Total Energy | 30.0 | J | ASTM D3763 |
| 23°C, Peak Energy | 24.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 86.7 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60, extruded sheet | 90 | ASTM D523 | |
| 60, thermoplastic | 25 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Melt Temperature | 216 - 241 | °C | |
| Die Temperature | 210 - 241 | °C | |
| Take-Off Roll | 73.9 - 93.3 | °C |
| Extrusion instructions |
|---|
| Compression Ratio: 2.5:1 to 2.7:1Pump Ratio: 1.5 to 2.0Max Regrind Allowed: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 126F2K4 | SAX Polymers | Nylon 6 | SAXAMID™ |
| Sylvin 6214-60D Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 4PROP® 9C11120 XHFR3 | 4Plas | PP Copolymer | 4PROP® |
| Daelim Po1y® PP-173 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Braskem PE HDB1052U1 | Braskem IDESA | HDPE | Braskem PE |