Lustran® ABS 248FC
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CE5nSe_Lustran-ABS-248FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS 248FC resin is a high-gloss, medium-impact grade of ABS (acrylonitrile butadiene styrene). This injection molding grade offers a good balance of physical properties and has been designed to be compliant with both medical and food contact regulations. Lustran ABS 248FC resin is used in applications requiring rigidity and intermediate abuse resistance. As with any product, use of Lustran ABS 248FC resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. Lustran ABS 248FC 000000 (natural) complies with FDA regulation 21 CFR 181.32 for repeated-use food-contact applications. It is also compliant with EU Directive 2002/72/EC and its amendments (2004/1/EC, 2004/19/EC, 2005/79/EC, 2008/39/EC) relating to plastic materials and articles intended to come into contact with foodstuffs. Lustran ABS 248FC resin is designated as "medical-grade" and has met the requirements of the USP Class VI and ISO 10993, Part I "Biological Evaluation of Medical Devices" tests with human tissue contact time of 30 days or less. Only medical-grade resins may be considered as candidates for applications requiring biocompatibility. . Regrind must not be used in medical applications requiring biocompatibility. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Specific Volume | 0.940 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2620 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 46.9 | MPa | ASTM D638 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 73.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 48 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 12.7mm | 93.3 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 86.1 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm, molded | 102 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 95.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 1 |
| CLTE - Flow (-30 to 30°C) | 8.1E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 266 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: ModerateDrying at 160°-170°F for 4 hours is also adequate. |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP8613 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Abistir® MR GF/17 NATURALE | SO.F.TER. SPA | ABS | Abistir® |
| ACCUTECH™ CP0437G30CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Generic Nylon 610 | Generic | Nylon 610 | Generic |
| LUVOCOM® 1105-8099/GY | LEHVOSS Group | PEEK | LUVOCOM® |