Bergamid™ A700 G40 H (f1)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CD7CAC_Bergamid-A700-G40-H-f1-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid™ A700 G40 H (f1) is a Polyamide 66 (Nylon 66) product filled with 40% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.45 | g/cm³ | DIN 53479 |
| Dimensional Stability | 0.0 | % | ISO 2796 |
| K-Value 2 | 74.0 to 78.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 3(23°C) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 215 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 90 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Maximum Use Temperature | IEC 60216 | ||
| -- 4 | 130 | °C | |
| Short Time | 220 | °C | |
| Melting Temperature (DSC) | 261 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.700 mm | 90.0 | °C | |
| 1.50 mm | 90.0 | °C | |
| 3.00 mm | 90.0 | °C | |
| RTI Imp | UL 746 | ||
| 0.700 mm | 90.0 | °C | |
| 1.50 mm | 90.0 | °C | |
| 3.00 mm | 90.0 | °C | |
| RTI Str | UL 746 | ||
| 0.700 mm | 100 | °C | |
| 1.50 mm | 105 | °C | |
| 3.00 mm | 110 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- | 21 | kV/mm | ASTM D149 |
| -- | 90 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.70 | IEC 60250 | |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.700 mm | PLC 0 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.700 mm | PLC 4 | ||
| 1.50 mm | PLC 2 | ||
| 3.00 mm | PLC 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | |||
| 0.700 mm, ALL | HB | UL 94 | |
| 1.50 mm, ALL | HB | UL 94 | |
| 3.00 mm, ALL | HB | UL 94 | |
| 3.00 mm, ALL | HB40 | IEC 60695-11-10, -20 | |
| 0.700 mm, ALL | HB75 | IEC 60695-11-10, -20 | |
| 1.50 mm, ALL | HB75 | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | ±0.03 g/cm³ |
| 2 . | 96% H2SO4 |
| 3 . | 1 mm/min |
| 4 . | Continuous (GTP 50% Tensile) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® HHM TR-258 | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Maxxam™ FR WC 0587-21 R2 RoHS | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| S&E PVC GPT-76-1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Hifax HKC 426P BLACK | LyondellBasell Industries | PP Homopolymer | Hifax |
| Zytel® MT409AHS NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |