Lumid® GP2200A(W)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CCby42_Lumid-GP2200A-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose Application HMID, SLMP B, Holder |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 147 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 6670 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 216 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 205 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Arc Resistance | 150 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 235 to 255 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure 5 | 0.981 to 2.94 | MPa | |
| Screw Speed | 60 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badaflex® TPE-S 40A 1588 | Bada AG | SEBS | Badaflex® |
| Boda BDF-H2751 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Formolene® 5144L | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Lion Idemitsu Composites PPS K532P1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Karina IVORY PVC COMPOUND -E 700-35/1-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |