Braskem PE SLL5405S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CCO68V_Braskem-PE-SLL5405S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SLL5405S is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good mechanical properties as well as sealability. This product has very low gel amount. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Additive: Antiblocking High Slip High Applications: Automatic Packaging (FFS); liners; general purpose; HDPE and LDPE blends. Process: Blown Film Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 1100 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1300 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm | 210 | MPa | ASTM D790 |
| 1% Secant, TD : 38 µm | 230 | MPa | ASTM D790 |
| Dart Drop Impact 1 | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 180 | g | ASTM D1922 |
| TD : 38 µm | 400 | g | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 87 | % | ASTM D6866 |
| Extrusion instructions |
|---|
| Blown Film Extrusion Temperature Profile: from 180 to 210°C Blow up Ratio: from 2 to 3:1 Die Gap: from 1.8 to 2.5 mm Screen Package: 40/40 - 100% pure 40/60/40 - Blend Mass Temperature: 190°C (max 210°C) |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-93A-B30 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Cheng Yu N66C3 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| HiFill® POM CO GF20 CC | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Lifoflex® UV 20 GC 1020 | ELASTO | SEBS | Lifoflex® |
| Karina BROWN PVC COMPOUND 809-36/467-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |