Minlon® 73GM40 NC010
| Category: | Nylon 6 , MINERAL REINFORCED NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Minlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CBtut6_Minlon-73GM40-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Mineral/Glass Reinforced Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 5.6 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.6 | -- | % | |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8300 | 4600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.5 | 4.0 | kJ/m² | |
| 23°C | 7.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 50 | kJ/m² | |
| 23°C | 60 | 65 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 4.0 | 5.5 | kJ/m² | |
| 23°C | 5.5 | 9.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 70.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.1E-5 | -- | cm/cm/°C | |
| Transverse | 7.7E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 33 | -- | kV/mm | IEC 60243-1 |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.013 | -- | ||
| 1 MHz | 3.8E-3 | -- | ||
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 55 | -- | mm/min | ISO 3795 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2070 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.23 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® PAC6-135 | Custom Resins Group | Nylon 66/6 | Nylene® |
| LG ABS SH625 | LG Chem Ltd. | ABS | LG ABS |
| Karina YELLOW COLOR CONCENTRATE 02/284-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lustran® Elite 1827 | Styrolution | ABS | Lustran® Elite |
| Padermid 6 GF30 N | TKC Kunststoffe e.K. | Nylon 6 | Padermid |