Nycast 6PA
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Cast Nylons Ltd. |
| Trademark: | Nycast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CBiglm_Nycast-6PA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Two of the most widely used cast nylons in the industry, NYCAST XHA BLUE and NYCAST 6PA NATURAL have delivered successful performance - with and without lubrication - in a variety of diverse applications, particularly as a bearing material. They are lightweight, offer extremely good wear resistance, high tensile strength and high modulus of elasticity. Other significant properties include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 to 1.17 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.50 to 0.60 | % | |
| Saturation | 5.0 to 6.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 to 125 | ASTM D785 | |
| Durometer Hardness (Shore D) | 78 to 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 to 3790 | MPa | ASTM D638 |
| Tensile Strength | 68.9 to 93.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 to 55 | % | ASTM D638 |
| Flexural Modulus | 2900 to 3450 | MPa | ASTM D790 |
| Flexural Strength | 107 to 121 | MPa | ASTM D790 |
| Compressive Modulus | 2240 to 2760 | MPa | ASTM D695 |
| Compressive Strength | 93.1 to 110 | MPa | ASTM D695 |
| Shear Strength | 68.9 to 75.8 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.22 | ASTM D1894 | |
| Deformation Under Load | 0.500 to 2.50 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 to 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 204 to 221 | °C | |
| 1.8 MPa, Unannealed | 93.3 to 204 | °C | |
| Continuous Use Temperature | 110 | °C | ASTM D794 |
| Melting Temperature | 227 to 238 | °C | |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ASTM D696 |
| Service Temperature - Intermittent | 166 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 to 24 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.70 | ||
| 1 kHz | 3.70 | ||
| 100 kHz | 3.70 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT2500-01UVA | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Amilan® CM1011G-45 | Toray Resin Company | Nylon 6 | Amilan® |
| Hostacom SB572C | LyondellBasell Industries | PP Copolymer | Hostacom |
| POLYfill PPH GF15030 PD2 | Polykemi AB | PP Homopolymer | POLYfill |
| Rotuba CAB B908 (13% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |