VESTAMID® HTplus M1033
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CBTz6g_VESTAMID-HTplus-M1033.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
VESTAMID HTplus M1033 is a glass-fiber reinforced (30%), heat-stabilized polyphthalamide compound (PPA) for injection molding. This base resin is especially suitable for manufacturing parts subjected to high temperature. VESTAMID HTplus M1033 is supplied as cylindrical pellets in polyethylene packaging. Drying at 120°C for at least 4 hours before processing is recommended. For information about processing of VESTAMID HTplus M1033, please follow the general recommendations for PPA in our information "Handling and Processing of VESTAMID HTplus." |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Complete Break | 7.0 | kJ/m² | |
| 23°C, Complete Break | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C, Complete Break | 40 | kJ/m² | |
| 23°C, Complete Break | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 313 | °C | ISO 306/A |
| -- | 284 | °C | ISO 306/B |
| Melting Temperature | 300 to 315 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 1965N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| EVICOM™ GL4/443 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| KOCETAL® DS500 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Karina BLACK PVC COMPOUND 670-DA-48/1 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Geon™ HTX Ultra LA436G | PolyOne Corporation | PVC Alloy | Geon™ HTX Ultra |