NANCAR® 1052M30
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CBTfYI_NANCAR-1052M30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 1052M30 is a medium high acrylonitrile butadiene copolymer with good oil resistance. It is a low Mooney version of NANCAR® 1052. The low Mooney provides optimum processing property in highly filled or reinforced compounds. NANCAR® 1052M30 , similar to NANCAR ® 1052, is an excellent multi-purpose nitrile elastomer. It is particularly recommended for shoes, transfer molding or extrusion and for frictioning or coating fabrics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | |
| Mooney Viscosity (ML 1+4, 100°C) | 33 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 33.0 | % | Internal Method |
| Solubility - in MEK | 100 | % | |
| Stabilizer | Non-staining |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.40 | % | ASTM D5688 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A 1 | 72 | ||
| Shore A 2 | 71 | ||
| Shore A 3 | 69 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 300% Strain 4 | 7.65 | MPa | |
| 300% Strain 5 | 8.83 | MPa | |
| 300% Strain 6 | 9.51 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield 7 | 25.2 | MPa | |
| Yield 8 | 23.8 | MPa | |
| Yield 9 | 22.2 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break 10 | 740 | % | |
| Break 11 | 680 | % | |
| Break 12 | 660 | % | |
| Tear Strength | 57.9 | kN/m | ASTM D624 |
| Compression Set 13(100°C, 70 hr) | 56 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 14(100°C, 70 hr) | 8.0 | % | ASTM D865 |
| Change in Ultimate Elongation in Air 15(100°C, 70 hr) | -26 | % | ASTM D865 |
| Change in Durometer Hardness in Air 16(Shore A, 100°C, 70 hr) | 7.0 | ASTM D865 | |
| Change in Tensile Strength 17 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | 5.0 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -11 | % | |
| Change in Ultimate Elongation 18 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -25 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -16 | % | |
| Change in Durometer Hardness 19 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 1.0 | ||
| Shore A, 100°C, 70 hr, in ASTM #3 Oil | -14 | ||
| Change in Volume 20 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | 0.20 | % | |
| 100°C, 70 hr, in ASTM Oil #3 | 21 | % |
| Note Message | |
|---|---|
| 1 . | Cured for 60.0 min at 150°C |
| 2 . | Cured for 40.0 min at 150°C |
| 3 . | Cured for 20.0 min at 150°C |
| 4 . | Cured for 20.0 min at 150°C |
| 5 . | Cured for 40.0 min at 150°C |
| 6 . | Cured for 60.0 min at 150°C |
| 7 . | Cured for 60.0 min at 150°C |
| 8 . | Cured for 40.0 min at 150°C |
| 9 . | Cured for 20.0 min at 150°C |
| 10 . | Cured for 20.0 min at 150°C |
| 11 . | Cured for 40.0 min at 150°C |
| 12 . | Cured for 60.0 min at 150°C |
| 13 . | Cured for 60.0 min at 150°C |
| 14 . | Cured for 40.0 min at 150°C |
| 15 . | Cured for 40.0 min at 150°C |
| 16 . | Cured for 40.0 min at 150°C |
| 17 . | Cured for 40.0 min at 150°C |
| 18 . | Cured for 40.0 min at 150°C |
| 19 . | Cured for 40.0 min at 150°C |
| 20 . | Cured for 40.0 min at 150°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 503 HB | RTP Company | SAN | RTP |
| METALCAP PPC371B73 | Polyram Ram-On Industries | PP Copolymer | METALCAP |
| Santoprene™ 201-73 | ExxonMobil Chemical | TPV | Santoprene™ |
| SUSTAPVDF FG | Röchling Sustaplast SE & Co. KG | PVDF | SUSTAPVDF |
| Europrene® SOL T 166 | Versalis S.p.A. | SBS | Europrene® |