Braskem PE SGM9450F
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CB5ehs_Braskem-PE-SGM9450F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bags in general (like T-shirt bags, Handle Bags, Star Bags, others); Geomembranes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 9.3 | g/10 min | |
| 190°C/5.0 kg | 0.33 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 13 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm, Blown Film | 40.0 | MPa | |
| TD : Yield, 13 µm, Blown Film | 30.0 | MPa | |
| MD : Break, 13 µm, Blown Film | 85.0 | MPa | |
| TD : Break, 13 µm, Blown Film | 45.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 13 µm, Blown Film | 590 | % | |
| TD : Break, 13 µm, Blown Film | 740 | % | |
| Dart Drop Impact 1(13 µm, Blown Film) | 250 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm, Blown Film | 58 | g | |
| TD : 13 µm, Blown Film | 51 | g | |
| Seal Initiation Temperature (13 µm, Blown Film) | 125 | °C | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 96 | % | ASTM D6866 |
| Puncture Resistance - Blown Film (12.5 µm) | 80.0 | J/m | Internal Method |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7308DL | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Retelan® SF NERO | SO.F.TER. SPA | ABS | Retelan® |
| TAIRIPRO K8802 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Evoprene™ HP 3710 | AlphaGary | SBC | Evoprene™ HP |
| PLUSTEK RA334G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |