Order Products : sales@su-jiao.com
Voltalef® 302
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | Arkema |
| Trademark: | Voltalef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CB1D4A_Voltalef-302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Voltalef® 302 is a Polytetrafluoroethylene (PTFE) product. It can be processed by extrusion, film extrusion, injection molding, or resin transfer molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2130 | kg/m³ | ISO 1183 1 |
| Water Absorption | ISO 62 2 | ||
| Saturation | 0.010 | % | |
| Equilibrium | 0.010 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 1400 | MPa | ISO 527-2 3 |
| Tensile Stress (Yield) | 43.0 | MPa | ISO 527-2 4 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2 5 |
| Nominal strain at break | > 50 | % | ISO 527-2 6 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength (23°C) | 80.0 | kJ/m² | ISO 179/1eA 7 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 8 | ||
| 0.45 MPa | 126 | °C | |
| 1.8 MPa | 70.0 | °C | |
| Glass Transition Temperature 9 | 55 | °C | ISO 11357-2 10 |
| Melting Temperature 11 | 214 | °C | ISO 11357-3 12 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 13 |
| Volume resistivity | 2.0E+12 | ohms·m | IEC 60093 14 |
| Electric strength | 21 | kV/mm | IEC 60243-1 15 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen index | 100 | % | ISO 4589-2 16 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 10 °C/min |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | 10 °C/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAFIN™ PB75 | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| NEOFLON™ RP-5000 | Daikin Fluorochemicals (China) Co., Ltd. | Fluoropolymer | NEOFLON™ |
| Axpoly® PS01 3039 | Axion Polymers | PS (HIPS) | Axpoly® |
| Fibremod™ GB402HP | Borealis AG | PP, Unspecified | Fibremod™ |
| LEXAN™ 9915A_ resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |