SABIC® PPcompound 8502
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CB0mt1_SABIC-PPcompound-8502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8502 is a modified mineral filled Polypropylene for automotive exterior applications. This material combines an excellent paint adhesion, high modulus, high impact and low density. SABIC® PPcompound 8502 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 19.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 12.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 40 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 9.0 | kJ/m² | |
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB30 BK EF | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| CERTENE™ PRM-35ARN | Muehlstein | PP Random Copolymer | CERTENE™ |
| Europrene® SOL R C2564-T | Versalis S.p.A. | SBR, Solution | Europrene® |
| Hostacom ERC 346N D | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ LUBRICOMP™ RL0049S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |