Stanyl® TS300
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CAg4eT_Stanyl-TS300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stanyl® TS300 is a Polyamide 46 (Nylon 46) material. It is available in Asia Pacific. Primary attribute of Stanyl® TS300: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.0 | -- | % | |
| Flow | 2.0 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 3300 | 1000 | MPa | |
| 120°C | 800 | -- | MPa | |
| 160°C | 650 | -- | MPa | |
| 180°C | 600 | -- | MPa | |
| 200°C | 500 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield | 100 | 55.0 | MPa | |
| Yield, 120°C | 50.0 | -- | MPa | |
| Yield, 160°C | 40.0 | -- | MPa | |
| Yield, 180°C | 35.0 | -- | MPa | |
| Yield, 200°C | 30.0 | -- | MPa | |
| Nominal Tensile Strain at Break | ISO 527-2 | |||
| -- | 40 | > 50 | % | |
| 120°C | > 50 | -- | % | |
| 160°C | > 50 | -- | % | |
| 180°C | > 50 | -- | % | |
| 200°C | > 50 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 3000 | 900 | MPa | |
| 120°C | 800 | -- | MPa | |
| 160°C | 600 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 10 | 35 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 10 | 35 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 8.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 20 | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PG30-01RD | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| KEBAFLEX® SG 60 HT A.01 black | BARLOG plastics GmbH | TES | KEBAFLEX® |
| TAFMER™ XM-5080S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |
| Sylvin 8749-80AM Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ SLX2571T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |