Heramid® A NER GF030/1K
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Heramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C9ocIi_Heramid-A-NER-GF030-1K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 30% glass fiber reinforced injection moulding grade. Heat stabilized. Black colour. Post-industrial grade produced with selected polymers coming from polymerization, fibres and compounding plants. ISO 1043 : PA66-T GF30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8500 | 6500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 130 | 85.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | 2.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 7500 | 4000 | MPa | ISO 178 |
| Flexural Stress 2 | 200 | 130 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 262 | -- | °C | ISO 11357 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 22HSP NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Forprene® 6SD001A65 | SO.F.TER. SPA | TPV | Forprene® |
| Glastic® 210 | Glastic Corporation | Polyester, TS | Glastic® |
| Ingeo™ AW 240D | NatureWorks® LLC | PLA | Ingeo™ |
| POLYCOMPO PP J830HV | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |