VENYL SE010 - 8696
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C9RIwO_VENYL-SE010---8696.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SE010 - 8696 is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.6 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.9 to 3.1 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 98 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2600 | 900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 55 | 210 | % | ISO 527-2 |
| Flexural Modulus | 2200 | 800 | MPa | ISO 178 |
| Flexural Stress | 115 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 25 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | -- | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 165 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 77.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 240 to 255 | °C | |
| Nozzle Temperature | 220 to 265 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 70.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILAMID® B3 TM2 | Nilit Plastics | Nylon 6 | NILAMID® |
| Greenflex® MP 34 | Versalis S.p.A. | EVA | Greenflex® |
| INNOPOL® PP CS 1-3830 MV | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Lion Idemitsu Composites PPS T531J1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| LNP™ THERMOCOMP™ KF002L compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ THERMOCOMP™ |