Latilon 28D K/40
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C9MIGN_Latilon-28D-K-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate (PC) based compound. Carbon fibre. Low smoke density and low toxicity index. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.15 to 0.30 | % | |
| Flow : 2.00 mm | 0.050 to 0.15 | % | |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 18000 | MPa | |
| 60°C | 17000 | MPa | |
| 90°C | 15500 | MPa | |
| 120°C | 14000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 135 | MPa | |
| Break, 60°C | 115 | MPa | |
| Break, 90°C | 100 | MPa | |
| Break, 120°C | 75.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.4 | % | |
| Break, 60°C | 1.5 | % | |
| Break, 90°C | 1.4 | % | |
| Break, 120°C | 1.6 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 135 | °C | |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ISO 11359-2 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Dimensional Stability | 76.0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A MV 14 SHI FR 1(f1) black 96.8106 | A. Schulman Europe | PBT | SCHULADUR® |
| Starflam AFR200Y | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| TORZEN® T2000HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Hifax CB 158 A | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| ISOTHANE® 1060AU | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |