HiPrene® MT41VD
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C8W4hp_HiPrene-MT41VD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® MT41VD is a 15% mineral filled, impact modified polypropylene compound suitable for injection moulding. This material has been developed for highly demanding aesthetic automotive application, with perfect scratch resistance and UV stabilization. It is especially suitable for car interior applications requiring ductility, because of its high impact resistance and requiring very high scratch resistance because of location in the car interior. This grade is available in natural or color-matched, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.90 | % | Internal method |
| Flow direction | 0.90 | % | Internal method |
| Ash Content (600°C) | 16 | % | ISO 3451 |
| Volatile Matter | 0.10 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Anti-scratch- Delta L 1 | 1.20 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 70 | mm/min | TL 1010 |
| Fogging 2(100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | g | VDA 277 | |
| Odor 3(80°C) | 2.40 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus 4(23°C) | 1750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 4.00 - 6.50 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumInjection Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | Performed on black plaques with rough structure, acc. PV 3952 |
| 2 . | 16 hr |
| 3 . | 2 hr, acc. PV 3900 |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LLDPE U8835 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| SLOVAMID® 66 W 30 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Stirol UPM-0612 L (1s.) | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| Arnite® T06 202 | DSM Engineering Plastics | PBT | Arnite® |
| LOFEX® A5110 | Lotte Chemical Corporation | PET | LOFEX® |