Badamid® B70 GK30 FR HF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C82s4h_Badamid-B70-GK30-FR-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®B70 GK30 FR HF is a polyamide 6 (nylon 6) material containing 30% glass beads. This product is available in Europe,. Badamid®The main characteristics of B70 GK30 FR HF are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5600 | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 95.0 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.0 | 6.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 5.0 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, not annealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 95.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | 6.20 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Short-Term Heat Resistance, IEC 216, 20000 hrs: 190°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 100°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| INEOS HDPE K46-06-185 | INEOS Olefins & Polymers USA | HDPE, HMW | INEOS HDPE |
| KPOL-HDPE HD K-0.30/960 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| Polene EVA MV1030 | TPI Polene Public Company Limited | EVA | Polene EVA |
| POLYCOMPO PP J702LB | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| Sumiliteresin® PR-53804 I | SBHPP | Phenolic | Sumiliteresin® |