Fiberfil® J-60/15/UV/HS is a Polypropylene Homopolymer (PP Homopolymer) material filled with 15% glass fiber. It is available in North America. Important attributes of Fiberfil® J-60/15/UV/HS are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.40 to 0.50 | % | |
| 6.35 mm | 0.50 to 0.60 | % | |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 to 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2760 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.5 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2600 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 149 | °C | |
| 1.8 MPa, Unannealed | 138 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF23BL6571 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Evoprene™ G 3292 | AlphaGary | SEBS | Evoprene™ G |
| Formolene® 6507N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| POLIMAXX 1126NK | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |
| Petrothene® GA694189 | LyondellBasell Industries | LLDPE | Petrothene® |