Hytrel® HTR8223 BK320
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C7lTZc_Hytrel-HTR8223-BK320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 42 Shore D High Viscosity Polyester Elastomer Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 9.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/10.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.6 | % | |
| Flow | 1.6 | % | |
| Water Absorption | |||
| 24 hr | 0.60 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 42 | ||
| Shore D, 15 sec | 38 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 75.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 26.0 | MPa | |
| 5.0% Strain | 3.50 | MPa | |
| 10% Strain | 5.50 | MPa | |
| 50% Strain | 10.0 | MPa | |
| 100% Strain | 13.0 | MPa | |
| 300% Strain | 19.0 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 680 | % | ISO 527-2 |
| Flexural Modulus | 79.0 | MPa | ISO 178 |
| Abrasion Resistance | 22.0 | mm³ | ISO 4649 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 130 | kN/m | |
| Flow | 120 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Partial Break | 110 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -50°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -100 | °C | ISO 974 |
| Glass Transition Temperature 1 | -50.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 195 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.7E-4 | cm/cm/°C | |
| Transverse | 1.7E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 9.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.0E-3 | ||
| 1 MHz | 0.013 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.00 | g/cm³ |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 799 X 112538 | RTP Company | HDPE | RTP |
| Mirakutoran® TPU XN-2001 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Elastollan® C59D | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| Generic PSU | Generic | PSU | Generic |
| LNP™ LUBRICOMP™ LCL36E compound | SABIC Innovative Plastics Europe | PEEK | LNP™ LUBRICOMP™ |