China PPS PTFE-hGR302
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C7fTpd_China-PPS-PTFE-hGR302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS/PTFE-hGR302 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows abrasive resistance, solvent resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage. Owing to its high performance, it's widely used in mechanical and chemical industry for making wearable parts/components which work in the high-temperature, high pressure and solvent circumstance. It's also an excellent candidate in aerospace field. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | Internal method |
| Molding Shrinkage - Flow | 0.25 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 136 | MPa | Internal method |
| Flexural Modulus | 10000 | MPa | Internal method |
| Flexural Strength | 200 | MPa | Internal method |
| Coefficient of Friction | 0.40 | Internal method | |
| Abrasion - Width | 6 | mm | Internal method |
| Abrasion Loss 1 | 6.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 13 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 272 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 6 to 12hr |
| Note Message | |
|---|---|
| 1 . | 120 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 7220 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Clariant ABS ABS4500G10 | Clariant Corporation | ABS | Clariant ABS |
| DAI-EL™ G-211 | Daikin Fluorochemicals (China) Co., Ltd. | Fluorelastomer | DAI-EL™ |
| Generic Phenolic - Glass Fiber | Generic | Phenolic | Generic |
| Sylvin 8240-80FU White 1508 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |