Vyncolit® W5020
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C6dtFz_Vyncolit-W5020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® W5020 is a glass bead and glass fiber reinforced phenolic molding compound with excellent mechanical and thermal properties, higher isotropic properties and good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Apparent Density | 0.67 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.36 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Post Shrinkage | 0.050 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.5 | % | ISO 178 |
| Tensile Modulus | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.85 | % | ISO 527-2 |
| Flexural Modulus | 13000 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Compressive Stress | 270 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 11 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 188 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 2.2E-5 | cm/cm/°C | |
| Transverse | 4.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.4E+13 | ohms | IEC 60093 |
| Volume Resistivity | 3.2E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC1F-4091 | Spartech Polycom | ABS | Spartech |
| Wellamid® MRGF25/15 42H-BK848 (Interior) | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Forflex® 72100IA85 | SO.F.TER. SPA | TPO (POE) | Forflex® |
| IROSTIC® S 6148 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |
| Vydyne® R525J BK0722 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |