Ebalta AH 120 / SR
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C6WY0T_Ebalta-AH-120-SR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 to 84 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3300 to 3900 | MPa | ISO 178 |
| Flexural Stress | 120 to 140 | MPa | ISO 178 |
| Compressive Stress | 95.0 to 115 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 46 to 66 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 to 91.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 23 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.10 to 1.14 | g/cm³ | |
| Viscosity (25°C) | 1.2 to 1.5 | Pa·s | |
| Curing Time (20°C) | 8.0 to 10 | hr | |
| Pot Life 1(20°C) | 16 to 18 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinelec CCB5834 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinelec |
| Vipel® F701-PTT-25 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| WELLAMID Nylon 6000 SCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Sylvin 8773-60D Brown 7377 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| LNP™ LUBRICOMP™ SCL36 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |