FORMULA P FIB 3610/L SC
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C6Ltkk_FORMULA-P-FIB-3610-L-SC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene compounded with 10% glass fiber. (provisional datasheet) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.55 - 0.66 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 35.0 | MPa | ISO 527-2 |
| Fracture | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 12 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 35 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Injection instructions |
|---|
| Drying Not Required |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellophane™ 600P23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| EXCELLOY CZ400 | Techno Polymer Co, Ltd. | PC+ABS | EXCELLOY |
| InnoClear™ OC-5070 | Innovative Polymers, Inc. | TSU | InnoClear™ |
| Karina IVORY PVC COMPOUND -E 800-35/ 1-Y-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAXAMID™ RC66G33HSL-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |