PRE-ELEC® ESD 7100
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C4gzRB_PRE-ELEC-ESD-7100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® ESD 7100 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 7100 has been developed for injection moulding and for the extrusion of thermoformable mono- or multi-layer sheet. The products made out of PRE-ELEC® ESD 7100 are washable, reusable and recyclable. Surface resistance values of 1e8 ohms (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters. Typical applications include trays, tote bins, crates and technical parts which give permanent ESD protection for the electronics, medical, pharmaceutical and paper handling industries. PRE-ELEC® ESD 7100 can be coloured into various bright colours. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 200°C/21.6 kg | 20 | g/10 min | ISO 1133 |
| 200°C/5.0 kg | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| -- | 0.50 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 35.2 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2 |
| -- | 26.9 | MPa | ASTM D638 |
| 4.00 mm | 27.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 28 | % | ASTM D638 |
| Fracture, 4.00mm | 28 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1790 | MPa | ASTM D790 |
| 4.00 mm | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 4.20 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 21.0 | kJ/m² | ASTM D256 |
| Notched Izod Impact 1 | ISO 180 | ||
| -20°C | 4.0 | kJ/m² | ISO 180 |
| 23°C | 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 50.4 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 69.4 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength 2 | ISO 180 | ||
| -20°C | 49 | kJ/m² | ISO 180 |
| 23°C | 68 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 87.8 | °C | ASTM D648B |
| 0.45 MPa, not annealed | 88.0 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | 100 | °C | ISO 306/A50, ASTM D1525 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+10 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Static Decay | |||
| -- | sec | ESD S20.20 | |
| -- | sec | IEC 61340-5-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Pressure | 75.2 - 120 | MPa | |
| Injection Rate | Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 200°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP1B20 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Chemical Resources GPPS600 | Chemical Resources, Inc. | PS (GPPS) | Chemical Resources |
| Flexalloy® 9100-65 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Lanufene LLF 183N | Ras Lanuf Oil & Gas Processing Company (RASCO) | LLDPE | Lanufene |
| Sylvin 8445-72FUV Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |