VALOX™ 7062HP resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C45WHZ_VALOX-7062HP-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ENDURAN 7062HP is a 38% mineral filled & FDA compliance injection moulding resin. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.81 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (266°C/1.2 kg) | 33 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 265°C/1.2 kg | 21.0 | cm³/10min | |
| 265°C/2.16 kg | 41.0 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.9 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.070 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 140 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4130 | MPa | ASTM D638 |
| -- | 4200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/5 |
| Break 3 | 55.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 5 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4480 | MPa | ASTM D790 |
| -- 7 | 3900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 110 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 74.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | 33 | kJ/m² | |
| 23°C | 37 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 26 | J/m | ASTM D256 |
| 23°C | 22 | J/m | ASTM D256 |
| -30°C 11 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 420 | J/m | ASTM D4812 |
| -30°C 13 | 30 | kJ/m² | ISO 180/1U |
| 23°C 14 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 5.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 69.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 15 | 65.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 175 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 16 |
| -- | 215 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 150°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 150°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.32 | W/m/K | ISO 8302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 245 to 270 | °C | |
| Processing (Melt) Temp | 255 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 120*10*4 mm |
| 16 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-80/10 | Techmer Engineered Solutions | Acetal (POM) Copolymer | TES |
| Vyncolit® BXE6952 | Vyncolit N.V. | Phenolic | Vyncolit® |
| LNP™ THERMOCOMP™ DF008ERH compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Softell TKG 300N C12716 | LyondellBasell Industries | PP Copolymer | Softell |
| TECHNYL STAR® S 218 MT40 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |