WanBlend® WHT-885ET8
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | WanBlend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C42lBB_WanBlend-WHT-885ET8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WHT-885ET8 is polyether-based TPU compound available in cylinder form that can solve a wide range of static decay, static shielding and electromagnetic shielding problems. Applications: Electronic component packaging, Pipes, Belts, Component trays, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 84 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 6.00 | MPa | |
| 300% Strain | 11.0 | MPa | |
| Tensile Strength | 26.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 710 | % | ASTM D412 |
| Tear Strength | 82.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -46.0 | °C | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+8 | ohms | ASTM D257 |
| Volume Resistivity | 5.0E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 190 | °C | |
| Injection Pressure | 70.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Die Temperature | 185 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® H050MN | Reliance Industries Limited | PP Homopolymer | REPOL® |
| ALTECH® PA6 C 2035/507 GF35 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| BUP 665 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| Karina ORANGE PVC COMPOUND 550D32/ 13-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TAFMER™ PN-0040 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |