RTP 700 GB 15
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C2hQfO_RTP-700-GB-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1170 | MPa | ASTM D638 |
| Tensile Strength | 17.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 965 | MPa | ASTM D790 |
| Flexural Strength | 18.6 | MPa | ASTM D790 |
| Compressive Strength | 19.3 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 72.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 51.7 | °C | ASTM D648 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 4.0E-3 | ASTM D150 | |
| Arc Resistance | 140 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in: 35mil/inTensile Elongation, ASTM D-638: >10% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 177 - 288 | °C | |
| Middle Temperature | 177 - 288 | °C | |
| Front Temperature | 177 - 288 | °C | |
| Mold Temperature | 23.9 - 51.7 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 116346 | RTP Company | PP, Unspecified | RTP |
| POLYMAN® (PC) XP 41 R 10 GF | A. Schulman Europe | PC | POLYMAN® |
| PRIMALLOY® B1700 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Multiuse Leostomer® LE-3160N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Hapflex™ 565 FR | Hapco Inc. | TP, Unspecified | Hapflex™ |