Zytel® 73G50HSLA BK416
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C2XsYp_Zytel-73G50HSLA-BK416.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% Glass Reinforced, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.58 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 4.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.4 | -- | % | |
| Viscosity Number | 135 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 15500 | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 233 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | 3.3 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 9400 | MPa | |
| 1000 hr | -- | 7300 | MPa | |
| Flexural Modulus | 14300 | 11100 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 19 | 18 | kJ/m² | |
| 23°C | 21 | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 100 | 90 | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 219 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 212 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 219 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 5.0E+12 | ohms | IEC 60093 |
| Comparative Tracking Index | 380 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB HB | -- | IEC 60695-11-10, -20 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.24 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2050 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.26 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPOLEN® FB 243-55 | MOL Petrochemicals Co. Ltd. | LDPE | TIPOLEN® |
| Hanwha Total PE 4220U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Latigloss 57 G/50 F2 | LATI S.p.A. | PPA | Latigloss |
| ICORENE® N2103 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |
| ESTOPLAST XU 150GY64 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |