INEOS PP L24G-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | C16HnI_INEOS-PP-L24G-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| L24G-00 is a high melt flow rate, antistated impact copolymer polypropylene offering excellent impact resistance and a high flexural modulus for applications in injection molding, consumer products, housewares, and automotive. This material has been recognized by UL for sustained use at 65°C and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 24.7 | MPa | |
| Break | 16.8 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 150 | % | |
| Flexural Modulus - 1% Secant 3 | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 53 | J/m | |
| 23°C | 190 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 5.30 | kJ/m² | |
| 23°C | 18.8 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Mixed | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.3 | °C | |
| 1.8 MPa, Unannealed | 50.6 | °C | |
| Vicat Softening Temperature | 149 | °C | ASTM D1525 |
| RTI Elec (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 79 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALGLASS H 07 H 20 G | RIALTI Srl | PP Homopolymer | RIALGLASS |
| TITANZEX® HI1600 | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANZEX® |
| XANTAR® MX 1061 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ICORENE® N2309 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| POCAN® B 1501 000000 | LANXESS GmbH | PBT | POCAN® |