SABIC® SUPEER™ 8318
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® SUPEER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BzLUGQ_SABICSUPEER8318.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® SUPEER™ 8318 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of high performance LLDPE cast film applications and has good impact strength and transparency. SABIC® SUPEER™ 8318 does not contain slip and anti-block agent. Application Typical applications for SABIC® SUPEER™ 8318 are stretch wrap film, silage film and breathable film. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : yield, 40 µm, extruded film | 9.80 | MPa | ASTM D882 |
| TD : yield, 40 µm, extruded film | 9.50 | MPa | ASTM D882 |
| MD : broken, 40 µm, extruded film | 49.0 | MPa | ASTM D882 |
| TD : broken, 40 µm, extruded film | 54.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : broken, 40 µm, extruded film | 600 | % | ASTM D882 |
| TD : broken, 40 µm, extruded film | 650 | % | ASTM D882 |
| Dart Drop Impact 1(40 µm, cast film) | 400 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, cast film | 10 | g | ASTM D1922 |
| TD : 40 µm, cast film | 23 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 115 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (40.0 µm, cast film) | 2.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cast Film Melt Temperature | 250 - 300 | °C | |
| Properties have been measured on cast film of 40µm |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M40060 Series | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| Sanren Q200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Deco-Coat™ DC-2550 | Epoxies, Etc. | Epoxy | Deco-Coat™ |
| apilon 52® ETC 40 | API SpA | TPU-Polyether | apilon 52® |
| Monprene® SP-29969 | Teknor Apex Company | TPE | Monprene® |