Lupoy® 1621-02
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bycvr5_Lupoy-1621-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOY PC 1621-02 resin is designed for large injection stretch blow molding and extrusion blow molding parts. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2280 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 63.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 90 | % | |
| Flexural Modulus | 2410 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 45 | kJ/m² | ISO 179 |
| Notched Izod Impact 1(23°C, 3.20 mm) | 930 | J/m | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed 2 | 142 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed 3 | 128 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed 4 | 137 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 146 | °C | ISO 306/B50 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 0.25 mm Notch Depth |
| 2 . | 4 mm |
| 3 . | 3.2 mm |
| 4 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP553 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| SKYGREEN® JN100 | SK Chemicals | PCTG | SKYGREEN® |
| Kepital® TG-63 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Karina CLEAR PVC COMPOUND 80/204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1104-7471 | Lehmann & Voss & Co. | PEK | LUVOCOM® |