LNP™ LUBRICOMP™ KFL25 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bxy1ye_LNP-LUBRICOMP-KFL25-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* KFL25 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber, 10% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KFL-4025 Product reorder name: KFL25 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.96 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.19 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10200 | MPa | ASTM D638 |
| -- | 9880 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 85.9 | MPa | ASTM D638 |
| Break | 84.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.3 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 9110 | MPa | ASTM D790 |
| -- | 9200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 132 | MPa | ASTM D790 |
| -- | 131 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 290 | J/m | ASTM D4812 |
| 23°C 3 | 19 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.62 | J | ASTM D3763 |
| -- | 1.77 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 166 | °C | ASTM D648 |
| CLTE | |||
| Flow : -40 to 40°C | 8.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8212-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Celstran® PP-GF40-10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Clariant Nylon 6/6 BR-2025 BK | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Evatane® 28-800 | Arkema | EVA | Evatane® |
| Ecobarrier® 0918A | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |