Menzolit® SMC 0520
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BxmG2n_Menzolit-SMC-0520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 0520 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor heavy metals. Menzolit® SMC 0520 is a special SMC with significantly reduced density. The glass level has been selected to combine good moulding with sufficient strength and stiffness properties. Even without a specific fire retardant the fire retardancy level HB according the UL 94 is achieved. The product is suitable especially for applications calling for low weight and durability. Another typical application are isolating panels or mouldings that require higher strength and stiffness then standard isolating materials could provide. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.810 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.030 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 13.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 3000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 50.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.30 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 19 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | Internal Method |
| Glass Transition Temperature | 170 | °C | DSC |
| CLTE - Flow | 1.4E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.30 | W/m/K | ISO 8302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 155 | °C | |
| Injection Pressure | 3.00 to 7.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| reFlex™ 100 | PolyOne Corporation | Plasticizer, Bio-based | reFlex™ |
| Tarnoform® 300 TF05 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| TES J-70/30 NAT | Techmer Engineered Solutions | Nylon 66+PP | TES |
| Hostacom HKP 215D BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |
| NEOFLON™ NP-101 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |