RALUPOL® UP 2100

Category:	Polyester, TS , Thermoset Polyester
Manufacturer:	RASCHIG GmbH
Trademark:	RALUPOL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Bxkda7_RALUPOL-UP-2100.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Organically and inorganically filled Polyester moulding compound Low post-shrinkage, very good electrical values, good mechanical strength Primary application(s): Safety cut outs, Contactors, Switches This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)

General Information
Filler / Reinforcement	Organic\Inorganic
Features	Good Electrical Properties Good Strength Low Shrinkage
Uses	Electrical Parts Switches
Agency Ratings	EU 2002/96/EC (WEEE) EU 2006/122/EC
RoHS Compliance	RoHS Compliant
Forms	Granules
Processing Method	Compression Molding Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.65 to 1.85	g/cm³	ISO 1183
Apparent Density	0.75 to 1.00	g/cm³	ISO 60
Molding Shrinkage - Flow			ISO 2577
-- ¹	0.80 to 1.1	%
-- ²	0.70 to 1.0	%
Water Absorption (23°C, 24 hr)	< 1.2	%	ISO 62
Post Shrinkage ³	0.20 to 0.40	%	ISO 2577

Thermal	Nominal Value	Unit	Test Method
Maximum Service Temperature			IEC 60216
<50 h	190	°C
20,000 h	130	°C

Additional Information	Nominal Value	Unit
Compression Molding Molding Pressure	> 10.0	MPa
Compression Molding Temperature	165 to 180	°C

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus			ISO 527-2
Compression Molded	4000 to 6000	MPa
Injection Molded	5000 to 8000	MPa
Tensile Stress			ISO 527-2
Compression Molded	25.0 to 40.0	MPa
Injection Molded	40.0 to 50.0	MPa
Flexural Modulus			ISO 178
Compression Molded	6000 to 9000	MPa
Injection Molded	7000 to 10000	MPa
Flexural Stress			ISO 178
Compression Molded	50.0 to 80.0	MPa
Injection Molded	80.0 to 120	MPa
Compressive Stress	150 to 200	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
Compression Molded	1.0 to 2.0	kJ/m²
Injection Molded	1.5 to 2.5	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
Compression Molded	5.0 to 8.0	kJ/m²
Injection Molded	6.0 to 10	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, Unannealed	> 180	°C	ISO 75-2/A
8.0 MPa, Unannealed	80.0 to 120	°C	ISO 75-2/C
CLTE - Flow (50 to 100°C)	2.5E-5 to 4.5E-5	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.90 to 1.0	W/m/K	ASTM E1461

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+11 to 1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+12 to 1.0E+13	ohms·cm	IEC 60093
Electric Strength	20 to 30	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	7.00 5.00
1 MHz	6.00 4.00
Dissipation Factor			IEC 60250
100 Hz	0.60 to 0.80
1 MHz	0.030 to 0.050
Arc Resistance	PLC 4		ASTM D495
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.00 mm)	V-0		UL 94
Glow Wire Flammability Index	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature	850	°C	IEC 60695-2-13

Injection	Nominal Value	Unit
Middle Temperature	50.0 to 70.0	°C
Front Temperature	80.0 to 100	°C
Processing (Melt) Temp	100 to 115	°C
Mold Temperature	165 to 180	°C
Back Pressure	1.00 to 1.50	MPa
Screw Speed	70 to 100	rpm

Note Message
1 .	Compression Molded
2 .	Injection Molded
3 .	168 h / 110°C

Resin Grade	Manufacturer	Category	Trademark
PRL PPX-GP7	Polymer Resources Ltd.	PPE+PS	PRL
New-prene™ 6040B	Total Polymer Vision (Suzhou) Co., LTD	PP+EPDM	New-prene™
Colorite 12 Series 6812	Colorite Polymers	PVC, Unspecified	Colorite 12 Series
LUVOCOM® 1301/CF/10/GF/20/GK/20/BK100	Lehmann & Voss & Co.	PPS	LUVOCOM®
TECHNYL® C 216 V30 GREY 2294	Solvay Engineering Plastics	Nylon 6	TECHNYL®