Torelina® A610EA1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torelina® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BxMEFM_Torelina-A610EA1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torelina® A610EA1 is a Polyphenylene Sulfide (PPS) product filled with 60% glass\mineral. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.90 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.70 | % | |
| Flow : 3.00 mm 2 | 0.15 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 0.80 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 22000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 235 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 18 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.6E-5 | cm/cm/°C | |
| Transverse | 2.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 23 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.360 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 3(320°C, 1.00 mm) | 150 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 98 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB1000-PC | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| UMG ALLOY® FA-820CA | UMG ABS, Ltd. | ASA+PC | UMG ALLOY® |
| Altuglas® BS 215 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Iupital® FU2050 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Osterlene® LD-3-931 | Osterman & Company | LDPE | Osterlene® |