Shinko-Lac ABS 3302 is a high heat resistant grade of ABS that also features good processability and excellent mechanical properties. Typical applications of 3302 include car stereo speaker boxes, vacuum bottle pots and automotive console boxes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 0.35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.55 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 46.1 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 71.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 49 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 100 | °C | ASTM D648 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 200 - 250 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 200 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V937 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 2800B-50A | RTP Company | TPV | RTP |
| Staramide B28H | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| VITAMIDE® BF23YL6634 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| UNISOFT ADHESION™ AD-50A-OP-1-25 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT ADHESION™ |