Badamid® T70
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bwffoe_Badamid-T70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| For extrusion and injection moulding, high toughness, strength and stiffness, low water absorption, high melting point |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.5 to 7.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.6 to 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Yield, 23°C) | 100 | 90.0 | MPa | ISO 527-2/50 |
| Tensile Strain 2(Yield, 23°C) | 4.5 | 4.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | ISO 527-2/50 | |||
| 23°C 3 | 12 | -- | % | |
| 23°C 4 | -- | 12 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 12 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 6(23°C) | 100 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 7(23°C) | 7.0 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 8 | ||||
| 0.45 MPa, Unannealed | 120 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 9 | 295 | -- | °C | ISO 3146 |
| CLTE 10 | ISO 11359-2 | |||
| Flow | 6.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 90 | -- | °C | |
| some hours | 240 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 11 | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity 12 | 1.0E+13 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity 13(1 MHz) | 4.00 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.040 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 310 to 340 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80x10x4 mm |
| 8 . | 110x10x4 mm |
| 9 . | 10 K/min, Compound for moulding |
| 10 . | >=10x10x4 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® E 8354-19189-2 | Vyncolit N.V. | Epoxy | Vyncolit® |
| XYLEX™ X7300CL resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| NuSil MED-361 | NuSil Technology | Silicone | NuSil |
| FHR Polypropylene P6G2N-095 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Elastollan® B 60 A 12 ESD 000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |