Jamplast Ex-02 ABS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BvoR0x_Jamplast-Ex-02-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jamplast Ex-02 ABS is a low-gloss, medium-impact extrusion grade of ABS (acrylonitrile butadiene styrene). It provides a good balance between rigidity and impact strength, and has a stiff melt flow suitable for extrusion and thermoforming. Jamplast Ex-02 ABS is bright white natural pellet which is easy to color with ABS color concentrates. This resin is designed for either profile extrusion or substrate coextrusion and can be used alone or blended with a higher-impact resin. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.6 | g/10 min | |
| Molding Shrinkage - Flow | 0.55 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1830 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 37.2 | MPa | |
| Break | 34.5 | MPa | |
| Tensile Strain | |||
| Yield | 2.6 | % | ISO 527-2 |
| Break | 100 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact (23°C) | 46.0 | J |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -- | 22 | kJ/m² | |
| -- 1 | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.0 | °C | |
| 1.8 MPa, Unannealed | 79.0 | °C | |
| 1.8 MPa, Annealed | 102 | °C | |
| Vicat Softening Temperature | 107 | °C | |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | at Low Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3X2G10 | BASF Corporation | Nylon 66 | Ultramid® |
| Next Nylon 66 Prime Series PG40-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Geon™ 120 Series 120X400 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 120 Series |
| Hyundai EP Adhesives LE130A/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| LAPEROS® S150 | Polyplastics Co., Ltd. | LCP | LAPEROS® |